Glass is an amorphous (non-crystalline) solid material. Glasses are typically brittle, and often optically transparent. The most familiar type of glass, used for centuries in windows and drinking vessels, is soda-lime glass, made of about 75% silica (SiO2) plus Na2O, CaO, and several minor additives. Often, the term glass is used in a restricted sense to refer to this specific use. In science, however, the term glass is usually defined in a much wider sense, including every solid that possesses a non-crystalline (i.e. amorphous) structure and that exhibits a glass transition when heated towards the liquid state. In this wider sense, glasses can be made of quite different classes of materials: metallic alloys, ionic melts, aqueous solutions, molecular liquids, and polymers. For many applications (bottles, eyewear) polymer glasses (acrylic glass, polyethylene terephthalate) are a lighter alternative to traditional silica glasses. Glass, as a substance, plays an essential role in science and industry. Their chemical, physical, and in particular optical properties make them suitable for applications such as flat glass, container glass, optics and optoelectronics material, laboratory equipment, thermal insulator (glass wool), reinforcement materials (glass-reinforced plastic, glass fiber reinforced concrete), and glass art (art glass, studio glass). 
Roman Cage Cup from the 4th century A.D. 
Oldest mouth-blown window-glass in Sweden (Kosta Glasbruk, 1742). In the middle is the mark from the glassblower’s pipe. 
Quartz sand (silica) is the main raw material in commercial glass production While fused quartz (primarily composed of SiO2) is used for some special applications, it is not very common due to its high glass transition temperature of over 2300 °C. Normally, other substances are added to simplify processing. One is sodium carbonate (Na2CO3), which lowers the glass transition to about 1500 °C. However, the soda makes the glass water soluble, which is usually undesirable, so lime (calcium oxide (CaO), generally obtained from limestone), some magnesium oxide (MgO) and aluminium oxide (Al2O3) are added to provide for a better chemical durability. The resulting glass contains about 70 to 74% silica by weight and is called a soda-lime glass. Soda-lime glasses account for about 90% of manufactured glass 
Following the glass batch preparation and mixing, the raw materials are transported to the furnace. Soda-lime glass for mass production is melted in gas fired units. Smaller scale furnaces for specialty glasses include electric melters, pot furnaces, and day tanks. After melting, homogenization and refining (removal of bubbles), the glass is formed. Flat glass for windows and similar applications is formed by the float glass process, developed between 1953 and 1957 by Sir Alastair Pilkington and Kenneth Bickerstaff of the UK’s Pilkington Brothers, who created a continuous ribbon of glass using a molten tin bath on which the molten glass flows unhindered under the influence of gravity. The top surface of the glass is subjected to nitrogen under pressure to obtain a polished finish. Container glass for common bottles and jars is formed by blowing and pressing methods. Further glass forming techniques are summarized in the table Glass forming techniques. Once the desired form is obtained, glass is usually annealed for the removal of stresses. Surface treatments, coatings or lamination may follow to improve the chemical durability (glass container coatings, glass container internal treatment), strength (toughened glass, bulletproof glass, windshields), or optical properties (insulated glazing, anti-reflective coating). 
A vitrification experiment for the study of nuclear waste disposal at Pacific Northwest National Laboratory. New chemical glass compositions or new treatment techniques can be initially investigated in small-scale laboratory experiments. The raw materials for laboratory-scale glass melts are often different from those used in mass production because the cost factor has a low priority. In the laboratory mostly pure chemicals are used. Care must be taken that the raw materials have not reacted with moisture or other chemicals in the environment (such as alkali oxides and hydroxides, alkaline earth oxides and hydroxides, or boron oxide), or that the impurities are quantified (loss on ignition). Evaporation losses during glass melting should be considered during the selection of the raw materials, e.g., sodium selenite may be preferred over easily evaporating SeO2. Also, more readily reacting raw materials may be preferred over relatively inert ones, such as Al(OH)3 over Al2O3. Usually, the melts are carried out in platinum crucibles to reduce contamination from the crucible material. Glass homogeneity is achieved by homogenizing the raw materials mixture (glass batch), by stirring the melt, and by crushing and re-melting the first melt. The obtained glass is usually annealed to prevent breakage during processing. 
A CD-RW (CD). Chalcogenide glasses form the basis of re-writable CD and DVD solid-state memory technology. Some glasses that do not include silica as a major constituent may have physico-chemical properties useful for their application in fibre optics and other specialized technical applications. These include fluoride glasses, aluminosilicates, phosphate glasses, borate glasses, and chalcogenide glasses. Glass-ceramic materials share many properties with both non-crystalline glass and crystalline ceramics. They are formed as a glass, and then partially crystallized by heat treatment. For example, the microstructure of whiteware ceramics frequently contains both amorphous and crystalline phases. Crystalline grains are often embedded within a non-crystalline intergranular phase of grain boundaries. When applied to whiteware ceramics, vitreous means the material has an extremely low permeability to liquids, often but not always water, when determined by a specified test regime. 
A high strength glass-ceramic cooktop with negligible thermal expansion. The term mainly refers to a mix of lithium and aluminosilicates which yields an array of materials with interesting thermomechanical properties. The most commercially important of these have the distinction of being impervious to thermal shock. Thus, glass-ceramics have become extremely useful for countertop cooking. The negative thermal expansion coefficient (TEC) of the crystalline ceramic phase can be balanced with the positive TEC of the glassy phase. At a certain point (~70% crystalline) the glass-ceramic has a net TEC near zero. This type of glass-ceramic exhibits excellent mechanical properties and can sustain repeated and quick temperature changes up to 1000 °C. From the 19th century, various types of fancy glass started to become significant branches of the decorative arts. Cameo glass was revived for the first time since the Romans, initially mostly used for pieces in a neo-classical style. The Art Nouveau movement in particular made great use of glass, with René Lalique, Émile Gallé, and Daum of Nancy important names in the first French wave of the movement, producing colored vases and similar pieces, often in cameo glass, and also using lustre techniques. Louis Comfort Tiffany in America specialized in secular stained glass, mostly of plant subjects, both in panels and his famous lamps. From the 20th century, some glass artists began to class themselves as in effect sculptors working in glass, and as part of the fine arts. 
Paperweight with items inside the glass, Corning Museum of Glass 
A glass sculpture by Dale Chihuly, “The Sun†at the “Gardens of Glass†exhibition in Kew Gardens, London. The piece is 13 feet (4 metres) high and made from 1000 separate glass objects. 
Glass tiles mosaic (detail).
From Wikipedia, the free encyclopedia : Wholesale glass, porcelain and pottery and in cleaning |